BITUFUG® WR 6 Fuge vergus mass

Bituminous hot sealing compound for cracks

The joint sealing compound BITUFUG® WR 6 corresponds to:

• the requirements of SNV 671625 a (KBH)
  
• the requirements of SS-S-164 (double specification)
  
• the requirements of the technical contract terms and guidelines for joints in traffic areas ZTV Fug-StB 15

processing

For casting joints from 5 - 6 mm wide on concrete roadways, asphalt surfaces, motorways, federal roads, airfields, etc. BITUFUG® WR 6 for increased cold and heat stress. The joints should be cleaned with a sweeper, and then blown out or vacuumed with compressed air. Freedom from dust and dryness of the joints are and will remain essential prerequisites for a good seal. In the case of renovations (renewal of the grout), the remains of old compound must also be removed and the joint flanks must be free of any concrete after-treatment agents, otherwise adhesion impairments may occur.

melting

Melting should only be done in a motor-driven stirrer cooker. When melting the shattered blocks of mass, heat slowly. The temperature of 180° C must be maintained with constant stirring or circulation. Temporarily exceeding or falling below this temperature of 10% is not important for our products. However, exceeding 200°C should be avoided. Due to its high binder content, the mass becomes viscous at low temperatures and no longer "runs" (risk of lumps or cavity formation in the joint = later sagging!), whereas at high temperatures the mass becomes too thin and "like water " runs (risk of segregation in the boiler = sinking and burning of the fillers and additives added for stabilization and tempering).

weather

It should only be cast in dry weather and at temperatures above 5°C. As the mass cools, it collapses, so it must be filled with supernatant. If additional pouring is required, this should be done onto the shiny, clean surface of the first pour.

Characteristics

• good permanent plasticity
• excellent heat resistance
• excellent cold resistance
• high resistance to aging and weathering
• very high adhesion to concrete, asphalt and various metals
• low surface tack at normal outside temperatures

weather

The work should only be carried out in dry weather and at temperatures above 5°C. The material contracts as it cools. For this reason, the sealing compound must be installed with an overhang. Necessary recasting work should be done on the shiny, clean surface of the first cast.

material consumption

Joint length (cm) x joint width (cm) x joint depth (cm) x density of joint compound (g/cm³) = consumption in grams
The consumption of BITUSOL-Voranstrich is approx. 3% of the casting compound requirement. Processing temperature:
approx. 150 - 180°C Density: approx. 1.10 g/cbm

form of delivery

Please note that the information in this publication corresponds to our current knowledge. Due to the large number of possible influences when processing and using our products, they do not release the processor from carrying out his own tests. A legally binding assurance of certain properties or the suitability for a specific purpose cannot be derived from our information. Existing laws and regulations are the responsibility of the recipient of our products.